低温氟碳乳液对丙烯酸类屋面防水涂料的改性效果实用性探究()
分享到：

《大众科技》[ISSN:1008-1151/CN:45-1235/N]

卷:
25
期数:
2023年8
页码:
53-57
栏目:
轻工与化工
出版日期:
2023-08-20

文章信息/Info

Title:
Practical Exploration on Modification Effect of Low-Temperature Fluorocarbon Lotion on Acrylic Roof Waterproof Coating
作者:
夏文秀1　曹志强1　薛兴勇2　陈发忠1　吴　睿1　覃向前3　宋漫玲1　
（1.广西产研院生物制造技术研究所有限公司，广西 南宁 530201；2.广西民族大学，广西 南宁 530007；3.广西青龙化学建材有限公司，广西 南宁 532700）
关键词:
低温氟碳乳液; 丙烯酸防水涂料; 改性; 实用性探究
Keywords:
low-temperature fluorocarbon lotion;  acrylic waterproof coating;  modification;  practical exploration
文献标志码:
A
摘要:
目的：在丙烯酸类防水涂料中加入水性氟碳乳液，研究其合适的物料比，以及不同配比对防水涂料的性能的影响，发现性能更优、成本合适的氟碳丙烯酸防水涂料的配方配比。方法：将丙烯酸类防水涂料传统配方中的丙烯酸乳液和四种氟碳乳液按不同比例配比混合，不断调节配制不同乳液配比的混合乳液，测量制得样品的粘度、拉伸强度、延伸率、低温柔性。结果：（1）添加2.5%～5%的RF-101、RF-102、T-912N氟碳乳液时，成膜后的测试结果拉伸强度较高，延伸率较低，低温柔性较低，其余组在原配方中增加400目碳酸钙百分比含量后得到的效果类似；（2）在防水乳液中添加2.5%～30%的氟碳乳液的各组丙烯酸防水涂料，最高的延伸率达到了377.04%，最高的拉伸强度达到了2.326 MPa，有一实验组达到了-22℃的低温柔性测试而不断裂，制成的实验膜进行干化时其延伸率和拉伸强度会出现程度不同的变化，性能符合国家标准。结论：在CF-809氟碳乳液满足改性要求的配比条件下，当氟碳乳液添加量达5%时，得到的产品低温性能有明显提高。
Abstract:
Objective: To add waterborne fluorocarbon lotion into acrylic waterproof coating, study its appropriate material ratio and the influence of different ratios on the performance of waterproof coating, and find out the formula ratio of fluorocarbon acrylic waterproof coating with better performance and appropriate cost. Methods: The acrylic lotion and four fluorocarbon lotion in the traditional formula of acrylic waterproof coating were mixed in different proportions, and the mixed lotion with different lotion proportions were continuously prepared. The viscosity, tensile strength, elongation and low-temperature flexibility of the samples were measured. Results: (1) When 2.5%~5% RF-101, RF-102, T-912N fluorocarbon lotion was added, the test results after film formation showed that the tensile strength was high, the elongation was low, and the low-temperature flexibility was low. The results of other groups were similar after adding 400 mesh calcium carbonate percentage content in the original formula; (2) Each group of acrylic waterproof coatings added with 2.5%~30% fluorocarbon lotion in the waterproof lotion has the highest elongation of 377.04% and the highest tensile strength of 2.326 MPa. One experimental group has reached the low-temperature flexibility test at -22 ℃ without breaking. When the experimental membrane is dried, its elongation and tensile strength will change to different degrees, and its performance meets the national standards. Conclusion: Under the condition that the ratio of CF-809 fluorocarbon lotion meets the modification requirements, when the addition amount of fluorocarbon lotion reaches 5%, the low-temperature performance of the obtained product is significantly improved.

参考文献/References:

[1]　文武，陈炳耀，温海军，等. 水性建筑防水涂料的性能、应用及发展[J]. 化工管理，2018(7): 94-95. [2]　王晓明. 水性丙烯酸树脂涂料的研究[D]. 南京: 南京航空航天大学，2012.[3]　董艳春，郑铁英，柳维成. 交联固化型氟碳漆与丙烯酸聚氨酯涂料性价比较[J]. 全面腐蚀控制，2012，26(4): 8-13.[4]　陈超峰. 丙烯酸材料在屋面防水层中的应用研究[D]. 重庆: 重庆交通大学，2018.[5]　林梓豪，陈炳耀，周义. 高弹丙烯酸防水涂料的制备及其施工方法[J]. 山东化工，2019，48(21): 107-108.[6]　文康. 水性丙烯酸树脂涂料的改性研究进展[J]. 石化技术，2019(11): 226，228.[7]　季兴宏. 水性氟碳弹性外墙涂料的制备及性能研究[J]. 涂层与防护，2018，39(7): 6-8，15.[8]　杨超，王云普，郭金山，等. 水性叔氟外墙涂料的研究[J]. 现代涂料与涂装，2007(10): 25-27[9]　吴建成. 水性氟碳应用介绍[J]. 涂层与防护，2018，39(1): 46-50.[10] 梁光容，陈炳耀，姚荣茂，等. 水性氟碳外墙涂料的性能研究[J]. 现代涂料与涂装，2020，23(2): 19-22.[11] 吴银萍. 单组分丙烯酸防水涂料的制备及性能研究[J]. 新型建筑材料，2020，47(5): 116-119.[12] JC/T 864－2008. 聚合物乳液建筑防水涂料[S]. 北京: 中国建筑工业出版社，2008.[13] GB/T 16777－2008. 建筑防水涂料试验方法[S]. 北京: 中国建筑工业出版社，2008.[14] 杨金星，陈炳耀，姚荣茂，等. 水性外墙氟碳涂料的研究[J]. 现代涂料与涂装，2020，23(8): 1-3，15.[15] GB/T 23445－2009. 聚合物水泥防水涂料[S]. 北京: 中国建筑工业出版社，2009.[16] 张翔，艾九红，李彩云，等. 单组分丙烯酸Ⅰ型防水涂料探索研究[J]. 中国建筑防水，2021(11): 1-5.

备注/Memo

备注/Memo:
【收稿日期】2023-04-13【作者简介】夏文秀（1989－），女，广西产研院生物制造技术研究所有限公司高级工程师，硕士，研究方向为化学防水涂料。【通信作者】覃向前（1998－），男，广西青龙化学建材有限公司助理工程师，研究方向为新型建筑防水材料。
更新日期/Last Update: 2023-08-24